Nanomaterials, MDPI AG, Vol. 12, No. 9 ( 2022-04-29), p. 1516-
Abstract:
Nitrogen-vacancy (NV) color centers in diamond are excellent quantum sensors possessing high sensitivity and nano-scale spatial resolution. Their integration in photonic structures is often desired, since it leads to an increased photon emission and also allows the realization of solid-state quantum technology architectures. Here, we report the fabrication of diamond nano-pillars with diameters up to 1000 nm by electron beam lithography and inductively coupled plasma reactive ion etching in nitrogen-rich diamonds (type Ib) with [100] and [111] crystal orientations. The NV centers were created by keV-He ion bombardment and subsequent annealing, and we estimate an average number of NVs per pillar to be 4300 ± 300 and 520 ± 120 for the [100] and [111] samples, respectively. Lifetime measurements of the NVs’ excited state showed two time constants with average values of τ1 ≈ 2 ns and τ2 ≈ 8 ns, which are shorter as compared to a single color center in a bulk crystal (τ ≈ 10 ns). This is probably due to a coupling between the NVs as well as due to interaction with bombardment-induced defects and substitutional nitrogen (P1 centers). Optically detected magnetic resonance measurements revealed a contrast of about 5% and average coherence and relaxation times of T2 [100] = 420 ± 40 ns, T2 [111] = 560 ± 50 ns, and T1 [100] = 162 ± 11 μs, T1 [111] = 174 ± 24 μs. These pillars could find an application for scanning probe magnetic field imaging.
Type of Medium:
Online Resource
ISSN:
2079-4991
DOI:
10.3390/nano12091516
Language:
English
Publisher:
MDPI AG
Publication Date:
2022
detail.hit.zdb_id:
2662255-5
Bookmarklink