Journal of Thermoplastic Composite Materials, SAGE Publications, Vol. 24, No. 6 ( 2011-11), p. 805-818
Abstract:
The fracture behavior of all-PP composites was studied under quasi-static loading conditions. Fracture toughness was evaluated by means of different fracture mechanics approaches depending on materials’ behavior. Composites consolidated at low temperature exhibited pop-in features and the failure occurs typically by delamination and tape stretching and fracture. With increasing consolidation quality – i.e., with increasing processing temperature – the delamination became less pronounced, and so the tape stretching occurred, before the specimens break. In composites consolidated at the highest temperature investigated (190°C), the laminate-like structure typical of self-reinforced composites produced according to film-stacking method was lost. Accordingly, composites behave as if they were only α-PP and β-PP matrices: α-rPP exhibited typical brittle fracture of α-PP, while β-rPP exhibited the stable behavior with fully yielded ligament before crack propagation commonly observed for β-PP. In general, stress–strain behavior changed from stable to unstable and fracture toughness strongly decreased as consolidation quality increased. Based on these results and previous findings, it can be concluded that the properties of self-reinforced PP composites can be tailored for a given application through the quality of consolidation.
Type of Medium:
Online Resource
ISSN:
0892-7057
,
1530-7980
DOI:
10.1177/0892705711401850
Language:
English
Publisher:
SAGE Publications
Publication Date:
2011
detail.hit.zdb_id:
2098671-3
Bookmarklink