In:
ECS Meeting Abstracts, The Electrochemical Society, Vol. MA2014-02, No. 7 ( 2014-08-05), p. 517-517
Abstract:
Lithium-ion batteries (LIBs) have surpassed any other battery technology for consumer electronics and mobile devices in the last decades mostly due to the high energy density and the lack of memory effect. Following the invention of the concept, a lot of effort has been put into improving the energy, the power as well as the safety of the LIBs. [1] Besides other aspects, the flammability of carbonates, frequently used as electrolyte components in most batteries, is one of the major drawbacks. There are different approaches to overcome this problem. One approach is to replace the liquid electrolytes with, for example ionic liquids, gel polymer electrolytes or even solid electrolytes. [2] . In another approach flame retardants (FRs) are added to suppress the flammability of the electrolyte to the point at which it becomes non-flammable for example phosphorous containing compounds. [3] Xu et al. tested different phosphate containing compounds with varying concentrations.[4, 5] This work displays a comparison study on five phosphorous containing FRs. The main goal was to gain deeper insight into the correlation between the fluorine content of the phosphate and the flammability of the electrolyte mixture. Special focus of the study was laid upon the fluorine content of the terminal carbon of the side chains. Electrolyte compositions with different concentrations of the FRs were prepared using standard electrolyte components with 1 M Lithium hexafluorophosphate as conducting salt and a mix of carbonates as solvent. Since the goal was to improve the flammability of the electrolyte the crucial investigation is depicted by the self-extinguishing time (SET), which is a common way in literature to display the flammability of a certain liquid. To test the possible use of the mixtures in LIBs constant current cycling experiments were performed in half-cells on anode material (T44 graphite) as well as on cathode material (LiNi 1/3 Mn 1/3 Co 1/3 O 2 (NMC)). Physical properties like the flashpoint, the viscosity and the ionic conductivity completed the measurements. Figure 1 displays the flammability of the tested electrolytes and the content in % is plotted vs the self-extinguishing time (SET) in s/g. It was shown that the tested phosphates have potential for application as components in non-flammable electrolytes, which yields in an increase in safety without a big trade-off in performance. [1] J. Wen, Y. Wen, C. Yu, J. Chen, Wen, Materials express, 2 (2012) 197-212. [2] J.B. Goodenough, Y. Kim, Chem Mater, 22 (2010) 587-603. [3] A. Granzow, Accounts Chem Res, 11 (1978) 177-183. [4] K. Xu, J Electrochem Soc, 150 (2003) A161. [5] K. Xu, M.S. Ding, S.S. Zhang, J.L. Allen, T.R. Jow, J Electrochem Soc, 149 (2002) A622-A626.
Type of Medium:
Online Resource
ISSN:
2151-2043
DOI:
10.1149/MA2014-02/7/517
Language:
Unknown
Publisher:
The Electrochemical Society
Publication Date:
2014
detail.hit.zdb_id:
2438749-6
Bookmarklink