Journal of Applied Physics, AIP Publishing, Vol. 93, No. 8 ( 2003-04-15), p. 4776-4783
Abstract:
Asymmetric metal–ferroelectric–metal (MFM) structures were manufactured by sol–gel deposition of a lead zirconate-titanate (PZT with Zr/Ti ratio 65/35) film on Pt-coated Si, with a Au top electrode. The average remnant polarization of 9 μC/cm2 and the coercive field of 39 kV/cm were obtained from the hysteresis loop measurements. A detailed analysis of the polarization–electric field (P–E), capacitance–voltage (C–V), and current–voltage (I–V) measurement results allowed us to estimate the near-electrode space-charge region thickness (roughly half of the film thickness at zero voltage), net doping concentration (around 1018 cm−3), built-in potential (in the 0.4–0.8 V range, depending on the injecting electrode), and dynamic dielectric constant (5.2). The current logarithm–voltage dependence for the field-enhanced Schottky emission obeys a “1/4” law. The spectral distribution of the short circuit current measured under continuous light illumination in the 290–800 nm range exhibits a cutoff wavelength at 370 nm and a maximum sensitivity at about 340 nm. The estimated band-gap energy of the PZT material is 3.35 eV. The MFM structure is discussed in terms of two back-to-back Schottky diodes with a ferroelectric material in between. It is concluded that the semiconductor properties of the films are not negligible and, in certain conditions, are dominating over the ferroelectric ones.
Type of Medium:
Online Resource
ISSN:
0021-8979
,
1089-7550
Language:
English
Publisher:
AIP Publishing
Publication Date:
2003
detail.hit.zdb_id:
220641-9
detail.hit.zdb_id:
3112-4
detail.hit.zdb_id:
1476463-5
Bookmarklink