Materials Science Forum, Trans Tech Publications, Ltd., Vol. 993 ( 2020-5), p. 321-326
Abstract:
The second phase dissolution of Al-9.2Zn-2.0Mg-1.9Cu alloy conducted by various temperatures of 2h was researched with the help of optical microscope (OM), scanning electron microscope (SEM), energy dispersive spectroscopy (EDS), electrical conductivity and differential scanning calorimetry (DSC) analysis. The results gave rise to the second phase existence of Mg(Zn,Cu,Al) 2 and Fe-containing phases in the as-extruded alloy. When the alloy solution treated with a temperature varied from 450°C to 470°C, a small quantity of Mg(Zn,Cu,Al) 2 phase still existed in the alloy while its content exhibited a decrement trend with the solution temperature rose. For the alloy solution treated at a temperature of 475°C, Mg(Zn,Cu,Al) 2 phase dissolved into the matrix completely while Fe-containing phase still remained. The electrical conductivity of quenched alloy decrease with the solution temperature increase and reached a minimum value at 470°C, and then rose slightly for the solution temperature of 475°C.
Type of Medium:
Online Resource
ISSN:
1662-9752
DOI:
10.4028/www.scientific.net/MSF.993
DOI:
10.4028/www.scientific.net/MSF.993.321
Language:
Unknown
Publisher:
Trans Tech Publications, Ltd.
Publication Date:
2020
detail.hit.zdb_id:
2047372-2
Bookmarklink