Japanese Journal of Applied Physics, IOP Publishing, Vol. 38, No. 3R ( 1999-03-01), p. 1506-
Abstract:
The compounds CsVTeO 5 and CsVTeO 6 have
been synthesized by solid-state reactions in an oxygen flow. CsVTeO 6 was decomposed to CsVTeO 5 at 550°C,
and this CsVTeO 5 was re-transformed into CsVTeO 6 under high oxygen pressure. The local structure around vanadium
and its valence state have been studied by X-ray absorption near edge structure spectroscopy at the vanadium K -edge.
CsVTeO 6 shows a weak peak at the pre-edge region, which
indicates that the vanadium is stabilized in an octahedral site as expected in normal AB 2 O 6 pyrochlore. On the other
hand, a strong pre-edge peak appeared in CsVTeO 5 as in
CsVO 3 and V 2 O 5 , which confirms that the local
symmetry around the vanadium atom is highly distorted without an inversion center. The Rietveld refinement shows that CsVTeO 5 has the cubic symmetry (space group Fd3m) with a = 10.4842(2) Å, which is similar to the high-temperature
polymorphic CsTiAsO 5 phase with highly distorted
octahedral symmetry around the titanium atom.
Type of Medium:
Online Resource
ISSN:
0021-4922
,
1347-4065
DOI:
10.1143/JJAP.38.1506
Language:
Unknown
Publisher:
IOP Publishing
Publication Date:
1999
detail.hit.zdb_id:
218223-3
detail.hit.zdb_id:
797294-5
detail.hit.zdb_id:
2006801-3
detail.hit.zdb_id:
797295-7
Bookmarklink