Abstract: The internal friction and dynamic modulus of Mo polycrystals were measured after fast neutron irradiation at liquid helium temperature. Similar measurements were also made on a Mo single crystal and Cu polycrystals for comparison purpose. It is found that the dislocation pinning in Mo started at about 30°K. This pinning process proceeded up to 80°K. During annealing above 80°K, the modulus change along with the change in the α‐peak was observed. The apparent difference between Mo and Cu in the pinning process is a continuous decrease in the thermal component of dislocation motion over a wider range of temperature in Mo.
Content:
Es wurde die innere Reibung und der Elastizitätsmodul von Mo‐Polykristallen nach Bestrashlung mit schnellen Neutronen bei Heliumtemperatur untersucht. Zum Vergleich wurden ähnliche Messungen auch an einem Mo‐Einkristall und an Cu‐Polykristallen durch‐geführt. Es wird gefunden, daß die Verankerung der Versetzungen in Mo bei etwa 30°K beginnt und sich bis zu 80°K erstreckt. Während der Temperung oberhalb 80°K wurde eine Moduländerung zusammen mit der änderung des α‐Maximums beobachtet. Der scheinbare Unterschied im Verankerungsprozeß zwischen Mo und Cu besteht in einer kontinuierlichen Abnahme der thermischen Komponente der Versetzungswanderung über einen größeren Temperaturbereich in Mo.
In:
volume:16
In:
number:2
In:
year:2006
In:
pages:355-364
In:
extent:10
In:
Physica status solidi. A, Applied research, Weinheim : Wiley-VCH, [1970-2004], 16, Heft 2 (2006), 355-364 (gesamt 10), 1521-396X
Language:
English
DOI:
10.1002/pssa.2210160202
URN:
urn:nbn:de:101:1-2405260623207.570549329353
URL:
https://doi.org/10.1002/pssa.2210160202
URL:
https://nbn-resolving.org/urn:nbn:de:101:1-2405260623207.570549329353
URL:
https://d-nb.info/1330724798/34
URL:
https://doi.org/10.1002/pssa.2210160202
Bookmarklink