Regular arrays of misfit dislocations at the interphase boundaries of a directionally solidified NiAl–Cr eutectic accommodate a certain amount of misfit between the chromium rods and the NiAl matrix. In this study the high temperature behaviour of these dislocation networks has been examined. Thin foils of the eutectic were heated slowly up to 700°C by a hot stage of the high voltage electron microscope and then cooled to room temperature. Investigations of bulk material quenched form 800° and 900°C complete the results. Although the misfit changes with temperature in consequence of different thermal expansions of the two phases the dislocation networks remain unchanged.
Content:
Abstract: Im gerichtet erstarrten NiAl–Cr‐Eutektikum wird ein bestimmter Betrag der Fehlpassung zwischen den Chromstäben und der NiAl‐Matrix durch regelmäßige Anordnungen von Anpassungsversetzungen abgebaut. In vorliegender Arbeit wurde das Verhalten dieser Versetzungsnetzwerke in einem größeren Temperaturintervall untersucht. Die Wärmebehandlung wurde einmal während der transmissionselektronenmikroskopischen Beobachtung dünner Folien (bis 700°C) zum anderen an kompakten Proben (bei 800° und 900°C) vorgenommen. Obwohl sich die Fehlpassung mit der Temperatur infolge der unterschiedlichen thermischen Ausdehnungskoeffizienten der beiden Phasen verändert, bleiben die beobachteten Versetzungsnetzwerke stabil.
In:
volume:12
In:
number:4
In:
year:2006
In:
pages:401-410
In:
extent:10
In:
Crystal research and technology, Weinheim : Wiley-VCH, 1966-, 12, Heft 4 (2006), 401-410 (gesamt 10), 1521-4079
Language:
English
DOI:
10.1002/crat.19770120410
URN:
urn:nbn:de:101:1-2405110450566.582369535725
URL:
https://doi.org/10.1002/crat.19770120410
URL:
https://nbn-resolving.org/urn:nbn:de:101:1-2405110450566.582369535725
URL:
https://d-nb.info/1328965600/34
URL:
https://doi.org/10.1002/crat.19770120410
Bookmarklink