Abstract: The various properties of the blends of polyacetal (POM) with up to 20 wt.‐% chemically surface‐treated poly (tetrafluoroethylene) (CPTFE) were investigated and compared with those of POM/PTFE blends. The PTFE is added to POM to improve the wear properties, however, the mechanical properties of POM/PTFE blends decrease with increasing PTFE content, but tensile strength and Young's modulus of POM/CPTFE blends are more than 2 times higher than that of the POM/PTFE blends. SEM shows that the size of inherent agglomerative PTFE is in the range of 30 to 100 μm. The particle size of major CPTFE dispersed in POM is smaller than 1 μm.
Content:
Die verschiedenartigen Eigenschaften von Polymerlegierungen aus Polyoxymethylen (POM) und bis zu 20 Gew.‐% chemische oberf;ächenbehandeltem Poly (tetrafluorethylen) (CPTFE) wurden untersucht und denen unbahandelter POM/PTFE‐ Blends gegenübergestellt. PTFE iwrd POM zugesetzt, um dessen Oberflächenabriebseigenschaften Anteil zunehmend verschlechtert. Durch die bessere Phasenanbindung in den oberflächenbehandelten POM/CPTFE‐ Blends konnten die doppelten Zugfestigkeiten und EModuli wie bei unbehandelten POM/PTEF‐ Blends erreicht werden. Mit Hilfe der Elektronenmikroskopie (SEM) konnte gezeigt werden, daß die PTEF‐Agglomerate in der POM‐Matrix eine Größe von 30 bis 100 μm haben, während die CPTFE‐Teilchengrößbe unter 1 μum liegt.
In:
volume:196
In:
number:1
In:
year:2003
In:
pages:21-35
In:
extent:15
In:
Die angewandte makromolekulare Chemie, Weinheim : Wiley-VCH, 1967-1999, 196, Heft 1 (2003), 21-35 (gesamt 15), 1522-9505
Language:
English
DOI:
10.1002/apmc.1992.051960102
URN:
urn:nbn:de:101:1-2024013104222143187433
URL:
https://doi.org/10.1002/apmc.1992.051960102
URL:
https://nbn-resolving.org/urn:nbn:de:101:1-2024013104222143187433
URL:
https://d-nb.info/1317723791/34
URL:
https://doi.org/10.1002/apmc.1992.051960102
Bookmarklink