In:
Scientific Reports, Springer Science and Business Media LLC, Vol. 7, No. 1 ( 2017-03-15)
Abstract:
The gel to carbonate precipitate route has been used for the synthesis of Ni 1−x Zn x Fe 2 O 4 (x = 0, 0.25, 0.5 and 0.75) bulk inverse spinel ferrite powder samples. The optimal zinc (50%) substitution has shown the maximum saturation magnetic moment and resulted into the maximum magnetic loss tangent (tanδ m ) 〉 −1.2 over the entire 2–10 GHz frequency range with an optimum value ~−1.75 at 6 GHz. Ni 0.5 Zn 0.5 Fe 2 O 4 - Acrylo-Nitrile Butadiene Rubber (NBR) composite samples are prepared at different weight percentage (wt%) of ferrite loading fractions in rubber for microwave absorption evaluation. The 80 wt% loaded Ni 0.5 Zn 0.5 Fe 2 O 4 /NBR composite (FMAR80) sample has shown two reflection loss (RL) peaks at 5 and 10 GHz. Interestingly, a single peak at 10 GHz for 3.25 mm thickness, can be scaled down to 5 GHz by increasing the thickness up to 4.6 mm. The onset of such twin matching frequencies in FMAR80 composite sample is attributed to the spin resonance relaxation at ~5 GHz ( f m1 ) and destructive interference at λ m /4 matched thickness near ~10 GHz ( f m2 ) in these composite systems. These studies suggest the potential of tuning the twin frequencies in Ni 0.5 Zn 0.5 Fe 2 O 4 /NBR composite samples for possible microwave absorption applications.
Type of Medium:
Online Resource
ISSN:
2045-2322
Language:
English
Publisher:
Springer Science and Business Media LLC
Publication Date:
2017
detail.hit.zdb_id:
2615211-3