Journal of Applied Physics, AIP Publishing, Vol. 90, No. 1 ( 2001-07-01), p. 506-508
Abstract:
We report abnormal ferroelectric properties of compositionally graded Pb(Zr,Ti)O3 thin films on LaNiO3-coated SiO2/Si substrates, where Pb(Zr,Ti)O3 and LaNiO3 films were prepared by a metalorganic decomposition technique and a sol–gel technique, respectively. It was found that the hysteresis loops of the Pb(Zr,Ti)O3 graded films measured by the conventional Sawyer–Tower method shifted along the polarization axis, i.e., they showed polarization offsets when applied by an alternating electric field. The polarization offsets were 82.5 μC/cm2 at 270 kV/cm and 62.5 μC/cm2 at 185 kV/cm for the up-graded film and the down-graded film, respectively. The absolute magnitude of the polarization offsets was closely related to the magnitude of the driving electric field, and the direction of the polarization offsets depended on the direction of the composition gradient with respect to the substrate. Analysis indicated that the polarization offsets did not originate from asymmetric contact effects, oxygen vacancies, alignment of defect dipoles, and/or electron injection. These results showed that polarization offsets in hysteresis loops were the intrinsic characteristic of the compositionally graded Pb(Zr,Ti)O3 thin films.
Type of Medium:
Online Resource
ISSN:
0021-8979
,
1089-7550
Language:
English
Publisher:
AIP Publishing
Publication Date:
2001
detail.hit.zdb_id:
220641-9
detail.hit.zdb_id:
3112-4
detail.hit.zdb_id:
1476463-5