AIP Advances, AIP Publishing, Vol. 5, No. 4 ( 2015-04-01)
Abstract:
Magnetite (Fe3O4) is an eligible candidate for magnetic tunnel junctions (MTJs) since it shows a high spin polarization at the Fermi level as well as a high Curie temperature of 585°C. In this study, Fe3O4/MgO/Co-Fe-B MTJs were manufactured. A sign change in the TMR is observed after annealing the MTJs at temperatures between 200°C and 280°C. Our findings suggest an Mg interdiffusion from the MgO barrier into the Fe3O4 as the reason for the change of the TMR. Additionally, different treatments of the magnetite interface (argon bombardment, annealing at 200°C in oxygen atmosphere) during the preparation of the MTJs have been studied regarding their effect on the performance of the MTJs. A maximum TMR of up to -12% could be observed using both argon bombardment and annealing in oxygen atmosphere, despite exposing the magnetite surface to atmospheric conditions before the deposition of the MgO barrier.
Type of Medium:
Online Resource
ISSN:
2158-3226
Language:
English
Publisher:
AIP Publishing
Publication Date:
2015
detail.hit.zdb_id:
2583909-3