In:
Japanese Journal of Applied Physics, IOP Publishing, Vol. 35, No. 6R ( 1996-06-01), p. 3414-
Kurzfassung:
Co–Cu binary alloys, whose Co concentrations range from 10 to 30 at.%, are produced by mechanical alloying. The structure, magnetoresistance (MR), and magnetism have been investigated for the as-milled and annealed alloys. After milling for 50 h, a supersaturated solid solution of fcc-CoCu is formed at Co concentrations of 10 to 30 at.%. The Co x Cu 100- x ( x = 10 – 30) alloys annealed at 700° C for 1 h separate into two phases of fcc-Co and fcc-Cu. The maximum MR ratio, under 15 kOe at room temperature, is 6.4% for the sample with x = 20 annealed at 450° C for 1 h. The samples annealed at temperatures less than 450° C exhibit high MR ratio at x = 25. The magnetism of the sample with x = 20, which shows a maximum MR ratio, exhibits superparamagnetic behavior, but a slight ferromagnetic behavior have also been observed. Co–Cu alloys produced by mechanical alloying have a wide distribution of Co particle size with blocking temperature from low temperature to room temperature.
Materialart:
Online-Ressource
ISSN:
0021-4922
,
1347-4065
DOI:
10.1143/JJAP.35.3414
Sprache:
Unbekannt
Verlag:
IOP Publishing
Publikationsdatum:
1996
ZDB Id:
218223-3
ZDB Id:
797294-5
ZDB Id:
2006801-3
ZDB Id:
797295-7