Dopant redistribution during gate oxidation in metal-oxide-semiconductor (MOS) fabrication processes has been studied by secondary-ion mass spectrometry (SIMS). In the first set of experiments, dopant profiles after gate oxidation are measured and compared to those after N 2 annealing. From the measured profiles, the contribution of oxidation-enhanced diffusion (OED) to the entire dopant redistribution is determined and an OED model parameter is calibrated. In the second set of experiments, samples which are subjected only to wafer loading and unloading steps are prepared and dopant profiles are measured. From the measured profiles, the magnitude of transient-enhanced diffusion (TED) which occurs during the wafer loading step is estimated and an interstitial-clustering parameter is calibrated. The parameters calibrated in this study are combined with the point-defect parameters taken from the literature, and dopant redistribution during the entire gate oxidation cycle is simulated. Calculated dopant profiles agree well with the measured SIMS profiles and show correct time dependence of TED and OED, as observed in the present experiments. In the simulations, interstitial concentration at the oxidizing Si/SiO 2 interface is found to be 40 times the equilibrium concentration. The supersaturation caused by surface oxidation is small and the contribution of OED is negligible under typical gate oxidation conditions where oxide thickness is less than 100 Å. Dopant profiles after gate oxidation are mainly dominated by TED. However, as oxidation proceeds, the contribution of OED increases because it continues while TED almost ends in the wafer loading step of gate oxidation. Segregation of boron in the channel region is also studied. It is found that a greater amount of boron is lost in oxidation than in N 2 annealing. The effect of segregation on device characteristics is not negligible for buried-channel PMOS devices, because the threshold voltage of the devices is sensitive to the change in the amount of boron.
Materialart:
Online-Ressource
ISSN:
0021-4922
,
1347-4065
DOI:
10.1143/JJAP.39.2565
Sprache:
Unbekannt
Verlag:
IOP Publishing
Publikationsdatum:
2000
ZDB Id:
218223-3
ZDB Id:
797294-5
ZDB Id:
2006801-3
ZDB Id:
797295-7