International Journal of Materials Research, Walter de Gruyter GmbH, Vol. 108, No. 2 ( 2017-02-10), p. 99-107
Abstract:
SA508Gr4 is a newly developed high-strength steel for nuclear reactor pressure vessels. Its welding characteristics remain largely unexplored. In this work, the simulated heat affected zone continuous cooling transformation (SH-CCT) diagram of SA508Gr4 steel was constructed and the high-temperature cooling phase compositions and the properties of the heat affected zone (HAZ) were characterized using dilatometry and microscopic tests. The results show that the phase transformation in the HAZ was divided into bainite and martensite transformation stages. When 4.6 ≤ t 8/5 (the HAZ cooling time from 800 °C to 500 °C) ≤ 15 s, lath-shaped martensite was fully developed, resulting in extensive hardening and cold cracking in the HAZ, while the cooling time required to form the bainite completely exceeds 1 200 s. Thus, to improve weld quality, preheating to 196 °C or higher is recommended.
Type of Medium:
Online Resource
ISSN:
2195-8556
,
1862-5282
Language:
English
Publisher:
Walter de Gruyter GmbH
Publication Date:
2017
detail.hit.zdb_id:
2232675-3
detail.hit.zdb_id:
2128058-7
detail.hit.zdb_id:
203021-4