Quantum Beam Science, MDPI AG, Vol. 6, No. 2 ( 2022-05-25), p. 21-
Abstract:
C-axis-oriented EuBa2Cu3O7−x oxide films that were 100 nm thick were irradiated with 0.5 MeV C monoatomic ions, 2 MeV C4 cluster ions and 4 MeV C8 cluster ions at room temperature. Before and after the irradiation, X-ray diffraction (XRD) measurement was performed using Cu-Ka X-ray. The c-axis lattice constant increased almost linearly as a function of numbers of irradiating carbon ions, but it rarely depended on the cluster size. Cluster size effects were observed in the XRD peak intensity and the XRD peak width. With increasing the cluster size, the decrease in peak intensity becomes more remarkable and the peak width increases. The experimental result implies that the cluster ions with a larger size provide a more localized energy deposition in a sample, and cause larger and more inhomogeneous lattice disordering. As such, local and large lattice disordering acts as a pinning center for quantum vortex; energetic carbon-cluster ion irradiation will be effective for the increment in the critical current of EuBa2Cu3O7−x superconductors.
Type of Medium:
Online Resource
ISSN:
2412-382X
Language:
English
Publisher:
MDPI AG
Publication Date:
2022
detail.hit.zdb_id:
2912215-6