In:
Key Engineering Materials, Trans Tech Publications, Ltd., Vol. 512-515 ( 2012-6), p. 319-322
Abstract:
Nano-porous SiO 2 insulation material was made from foamed aqueous slurry of nano-silica powder by filter-pressing. The foamed aqueous slurry mainly consists of hydrophobic SiO2 nano-particles, xonotlite whiskers and glass fiber. The latter two will enhance strength of the insulation material. Rheological properties of the foamed slurry with varying solid mass concentration were studied. The effect of forming pressure on the density and pore size distribution of the nano-porous silica material was investigated. It was found that the foamed slurry with solid concentration less than 17% behaves pseudoplastic as decreasing its apparent viscosity with increasing of shear rate during rheological testing. Homogeneous foamed slurry can be obtained when solid concentration in it is below 7%. Such slurry should be dewatered into solid concentration being of 10-15% before filter-pressing. Rigorously stirring of the concentrated slurry is required before pouring it into a mould, which leads to reducing the viscosity of the slurry and helps uniformly filling mould. During pressing the loading speed should be strictly controlled in order to reaching designed pore size distribution in SiO 2 insulation material. The SiO2 insulation material with apparent density about 0.45g/cm3 and pore size mainly ranging from 10 to 50nm was obtained.
Type of Medium:
Online Resource
ISSN:
1662-9795
DOI:
10.4028/www.scientific.net/KEM.512-515
DOI:
10.4028/www.scientific.net/KEM.512-515.319
Language:
Unknown
Publisher:
Trans Tech Publications, Ltd.
Publication Date:
2012
detail.hit.zdb_id:
2073306-9