Key Engineering Materials, Trans Tech Publications, Ltd., Vol. 645-646 ( 2015-5), p. 356-361
Kurzfassung:
A simple composite bonding that combines dielectric barrier discharge (DBD) plasma activation with anodic bonding has been developed to achieve strong silicon/glass bonding at low temperature. The realization of low temperature bonding is attributed to enhance the hydrophilicity and smooth of silicon and glass surfaces and form lots of free radical after the DBD plasma (including-OH, -H, O, and heat) reacts with the interfaces. And these further reduce the difficulty of chemical bond switching, and improve the speed of the intimate contact formation. The experimental result show that the bonding temperature strongly decreased 100°C by using composite anodic bonding with DBD pretreatment which strength kept constant, and 10MPa bonding strength was obtained at 250°C/900V after the bonding interface was treated for 10s under the conditions of AC1.5KV/25KHz and the clearance 100μm.
Materialart:
Online-Ressource
ISSN:
1662-9795
DOI:
10.4028/www.scientific.net/KEM.645-646
DOI:
10.4028/www.scientific.net/KEM.645-646.356
Sprache:
Unbekannt
Verlag:
Trans Tech Publications, Ltd.
Publikationsdatum:
2015
ZDB Id:
2073306-9