In:
Acta Physica Sinica, Acta Physica Sinica, Chinese Physical Society and Institute of Physics, Chinese Academy of Sciences, Vol. 49, No. 9 ( 2000), p. 1852-
Abstract:
In order to obtain a new kind of antiferroelectric (AFEt) ceramics wi th lower AFEt-Ferroelectric (FER) switching field Ef and less hysterisis loss ΔE for application of large displacement actuato r, Ba2+ ionics was employed to control the relative stability between AFEt, FER, and parroelelctrics (PEc) phases in (Pb097-xBaxLa002)(Zr055Sn035Ti01)O3 (0≤x≤02) system. Structural chan ges and electric properties as a function of Barium content x have been investig ated by X-Ray diffraction, dielectric properties, polarization and longitudinal strain measurement. It is observed that AFEt changes to FER, and finally to ferroelectric relaxors(RFE) as Ba content x increases from zer o to 02. Based upon these expermental result, we are able to tailor the AFE-FE switching parameters such as Ef, ΔE and AFEt operating t emperature range ΔT through modifying the Ti/Sn ratio near AFEt/FER phase boundary in the (Pb087Ba01La00 2)(Zr06TiySn04-y)O3 (004 ≤y≤009) system. Finally, a new kind of AFEt ceramics with Ef =16kV/mm，ΔE=085kK/mm， and longitudinal strain x=01%—02% which is appropriate for application of digital actuators has been obtained. Phase dia gram with composition located near AFEt/FER boundary of t he studied system has been determined.
Type of Medium:
Online Resource
ISSN:
1000-3290
,
1000-3290
Language:
Unknown
Publisher:
Acta Physica Sinica, Chinese Physical Society and Institute of Physics, Chinese Academy of Sciences
Publication Date:
2000